ABSTRACT: Magnetic and magnetoelastic measurements have been performed for Fe27.25Ni42.25Co17Si1.5B12 strips with lengths of 35, 30, 25 and 20 mm and widths of 5.0, 3.3, 2.5 and 1.7 mm. A saturation magnetization of 0.8 T was measured for the ribbons and the obtained saturation magnetostriction of 7 ppm was calculated for the best magnetoelastic case. Delta E effect was measured for all the different length strips and the obtained values were between 11.2 and 17.5 %, strongly influenced by the sizes and/or the length to width ratios. Finite element simulations were performed in order to study the mechanical behavior of the strips. Deflections under a pressure of 30 mbar and the first six vibration modes were simulated for all the ribbon sizes. The obtained experimental parameters were considered in the simulations to study the feasibility of the design of a gas valve using these metallic glass strips.
RESUMEN: Se han realizado medidas magnéticas y magnetoelásticas para cintas cuya composición obtenida fue Fe27.25Ni42.25Co17Si1.5B12, con longitudes de 35, 30, 25 and 20 mm y anchuras de 5.0, 3.3, 2.5 and 1.7 mm. Se ha medido una imanación de saturación de 0.8 T para todas las cintas. Se ha estimado una magnetostricción de saturación de 7 ppm para el mejor caso magnetoelástico. Para todas las longitudes y anchuras de las cintas se ha medido el efecto ∆E y los resultados obtenidos oscilaron entre el 11.2 y el 17.5 %, influenciados por los tamaños y/o la relación de aspecto. Se han realizado simulaciones de elementos finitos para estudiar propiedades mecánicas de las cintas. Se han simulado deflexiones bajo una presión de 30 mbar y los seis primeros modos de vibración para todos los casos. Estos parámetros determinados experimentalmente se utilizaron en las simulaciones para estudiar la viabilidad del diseño de una válvula de gas usando cintas de estos vidrios metálicos.