abstract = {The effect of intentionally introducing a large depolarization field in (001)-oriented, epitaxial Pb(Zr0.2TiO0.8)O3 (PZT) ultrathin films grown on La0.67Sr0.33MnO3 (LSMO) buffered SrTiO3 (STO) substrates is investigated. Inserting between 3 and 10 unit cells of STO between two 3 nm thick PZT films significantly influences the out-of-plane (c) lattice constant as well as the virgin domain state. Piezoresponse force microscopy images reveal a nanoscale (180°) polydomain structure in these films. In comparison, a “reference” single layer PZT sample (6 nm thick without STO spacer) exhibits an elongated PZT c-axis (0.416 nm) and is preferentially “down”-polarized with large regions of monodomain contrast. It shows asymmetric switching loops (i.e., imprint) coupled with sluggish domain switching under external bias. It is shown that the insertion of STO drives a monodomain to 180° polydomain transition in the as-grown state, which reduces the imprint by 80%. The insertion of the STO also profoundly improves dielectric leakage and hence the distribution of the applied electric field. Consequently, the critical pulse duration of the electric field required to initiate domain switching is reduced by two orders of magnitude relative to the reference sample. These results demonstrate the possibility of manipulating the depolarization field in such a way that it has positive effects on the ferroelectric behavior of ultrathin PZT films.},
organization = {Acknowledgements: G.L. and J.C. contributed equally to this work. G.L., J.C., and N.V. acknowledge support from ARC Discovery Project. N.V. acknowledges valuable discussions with Prof. P. Alpay and Prof. Anna Morozovska. C.L. and J.-M.T. thank support from the Swiss National Science Foundation division II. P.A.-P. and J.J. acknowledge the Spanish Ministry of Science and Innovation through the MICINN Grant FIS2012–37549-C05-04 and by the European Union through the project EC-FP7, Grant No. CP-FP 228989–2 “OxIDes.”},
publisher = {Wiley-Blackwell},
publisher = {Advanced Electronic Materials, 2016, 2(1), 15002881},
title = {Positive effect of an internal depolarization field in ultrathin epitaxial ferroelectric films},
author = {Liu, Guangqing and Chen, Jason and Lichtensteiger, Céline and Triscone, Jean-Marc and Aguado Puente, Pablo and Junquera Quintana, Francisco Javier and Valanoor, Nagarajan},
}